  • Pregunta: it is desired to obtain a hypoeutectoid steel with 42 HRC; propose tempering heat treatment; where 3 solid phases are formed. indicate the treatment conditions and the percentages of phases that will be formed

    it is desired to obtain a hypoeutectoid steel with 42 HRC; propose tempering heat treatment; where 3 solid phases are formed. indicate the treatment conditions and the percentages of phases that will be formedstudent submitted image, transcription available below

    Muestra el texto de la transcripción de la imagen
  • Chegg Logo
    Esta es la mejor manera de resolver el problema.
    Solución
    Te mostramos cómo abordar esta pregunta.

    First, determine the initial temperature for austenitization by identifying the temperature above which austenite forms, usually around , and ensure that the steel is fully austenitized by holding it at this temperature briefly.

    The previously shown graphic of carbon equilibria occurs only when the enfriamiento is very slow, which does not occur on an industrial scale.    As a result, I devised a TTT (transformation-time-temperat…

    Mira la respuesta completa
    answer image blur
Texto de la transcripción de la imagen:
3. (Valor 20 Puntos) Se desea obtener un acero hipoeutectoide con 42 HRC; proponga un tratamiento térmico de templado; donde se formen tres fases sólidas. Indique las condiciones del tratamiento y los porcentajes de fases que se formaran. Temperatura, °C 1000 900 800 700 600 500 400 300 200 100 0 A₁ Y 0,1 M₂ M. Austenita P. ✓P+T -- 1 B+y B₂ MtY P B Martensita 10 102 103 104 Tiempo, segundos 14 38 Dureza Rockwell C 66 105